| AFP
200 Paste |
Flux
type
|
Brazing
temperature |
Area
of brazing/welding
Properties
|
Base
metal |
Filler
metal |
Brazing
process |
DIN
8511:
F-LH 1
EN
1045:
FL 10
|
520
– 640 °C |
Hygroscopic
flux for open furnace brazing, well suitable for use with solder plated
base material and Al-alloys up to 2,5 % Mg.
Flux-residues must be removed after brazing.
|
Al
99,99
AlMn
AlMg
1
AlMgSi
0,5
AlMgSi
1
AlMg
2
|
Solder
plated base metal
Zetlot No.7
|
Oxyfuel
torch brazing
|
|
|
 |
| Supra
21 Powder |
Flux
type
|
Brazing
temperature |
Area
of brazing/welding
Properties
|
Base
metal |
Filler
metal |
Brazing
process |
DIN
8511:
F-LH 1
EN
1045:
FL 10
|
>
570 °C |
Hygroscopic
welding powder for gas fusion welding of aluminium and aluminium alloys
with magnesium-contents up to 2,2 %.
Flux-residues must be removed after welding.
|
Al
99,99
AlMn
AlMg
1
AlMgSi
0,5
AlMgSi
1
AlMgMn
AlMg
2
|
2s
4s
5s
|
Gas
fusion welding
TIG welding
|
|
|
|
| Magna
41 Powder |
Flux
type
|
Brazing
temperature |
Area
of brazing/welding
Properties
|
Base
metal |
Filler
metal |
Brazing
process |
DIN
8511:
F-LH 1
EN
1045:
FL 10
|
>
550 °C
|
Hygroscopic
welding powder also for gas fusion welding of aluminium and aluminium alloys
with magnesium-contents above 2,2 %.
Flux-residues must be removed after welding.
|
AlMg2
AlMgMn
AlMg3
G-AlMg3
G-AlMg
3 Si
G-AlMg5
G-AlMg
10
|
8s
805
|
Gas
fusion welding
TIG welding
|
|
|
|
| Platra
251 Powder |
Flux
type
|
Brazing
temperature |
Area
of brazing/welding
Properties
|
Base
metal |
Filler
metal |
Brazing
process |
DIN
8511:
F-LH 1
EN
1045:
FL 10
|
520
– 640 °C |
Hygroscopic
flux for open furnace brazing, well suitable for use with solder plated
base material and Al-alloys up to 2,0 % Mg.
Flux-residues must be removed after brazing.
|
Al
99,99
AlMn
AlMg
1
AlMgSi
0,5
AlMgSi
1
AlMg
2
|
Solder
plated base metal
Zetlot No.7
|
Oxyfuel
torch brazing
Open furnace bracing
|
|
|
|
| Platra
241 Powder |
Flux
type
|
Brazing
temperature |
Area
of brazing/welding
Properties
|
Base
metal |
Filler
metal |
Brazing
process |
DIN
8511:
F-LH 1
EN
1045:
FL 10
|
520
– 640 °C |
Hygroscopic
flux for open furnace brazing, well suitable for use with solder plated
base material and Al-alloys up to 2,5 % Mg.
Flux-residues must be removed after brazing.
|
Al
99,99
AlMn
AlMg
1
AlMgSi
0,5
AlMgSi
1
AlMg
2
|
Solder
plated base metal
Zetlot No.7
|
Oxyfuel
torch brazing
Open furnace bracing
|
|
|